Mechanical Strength and Mechanism Analysis of Silt Soil Cured by Straw Ash-Calcium Carbide Slag

Large-scale engineering projects frequently involve pit excavation and wetland landfill operations, resulting in significant silt accumulation that occupies land and adversely affects the environment. Curing technology offers a solution for reusing this waste silt. In this study, straw ash and calcium carbide slag are proposed as effective curing agents for silt soil. Various indoor tests were conducted to evaluate the mechanical properties of the cured silt soil, while X-ray diffraction (XRD) and scanning electron microscopy (SEM) were used to analyze its mineral composition and micro-morphology. The results showed that increasing the curing agent dosage significantly improved soil strength. Specifically, at a 10% dosage, the California bearing ratio (CBR) value increased to 18.7%, which is 13.4 times higher than untreated silt soil and exceeds road specifications by 8%. At a 20% dosage, the unconfined compressive strength (UCS) value reached 1.38 MPa, meeting the ≥0.8 MPa requirement for roadbeds. Based on economic considerations, a 20% dosage of straw ash-calcium carbide slag was selected as optimal. Microscopic analysis revealed that the addition of these agents promoted the formation of hydrated calcium silicate, filling pores and enhancing the mechanical properties of the cured soil, resulting in a more dense and stable structure.