The Multiferroic, Magnetic Exchange Bias Effect, and Photodetection Multifunction Characteristics in
Ye Zhao1, Ruilong Yang1,2, Ke Yang1
1School of Chemistry and Materials Science of Shanxi Normal University & Key Laboratory of Magnetic Molecules and Magnetic Information Materials, Ministry of Education, Taiyuan 030006, China.
Abstract:
Artificial heterostructures are typically created by layering distinct materials, thereby giving rise to unique characteristics different from their individual components. Herein, two-dimensional α-MnSe nanosheets with a non-layered structure were fabricated on Ga0.6Fe1.4O3 (GFO) films. The superior crystalline properties of MnSe/GFO heterostructures were confirmed through structural and morphological analyses. The remanent polarization is around 1.5 μC/cm2 and the leakage current density can reach 2 × 10-3 A/cm2 under 4 V. In addition, the piezo-response force microscopy amplitude and phase images further supported the ferroelectric property. The significant improvement of coercive field and saturated magnetization, along with the antiparallel signals of Mn and Fe ions observed through synchrotron X-ray analyses, suggest the presence of magnetic interaction within the MnSe/GFO heterostructure. Finally, the excellent photodetector with a photo detectivity of 6.3 × 108 Jones and a photoresponsivity of 2.8 × 10-3 A·W-1 was obtained under 532 nm in the MnSe/GFO heterostructure. The characteristics of this heterostructure, which include multiferroic, magnetic exchange bias effect, and photodetection capabilities, are highly beneficial for multifunctional devices.
Related Concept Videos
01:27Biasing of Metal-Semiconductor Junctions
In Schottky junctions, where the semiconductor is n-type, applying a positive voltage to the metal relative to the semiconductor reduces its Fermi...
03:02Colors and Magnetism
When atoms or molecules absorb light at the proper frequency, their electrons are excited to higher-energy orbitals. For many main group atoms and molecules, the absorbed photons are in the ultraviolet range of the electromagnetic spectrum, which cannot be detected by the human eye. For coordination compounds, the energy difference between the d orbitals often allows photons in the visible range to be absorbed and emitted, which is seen as colors by the human...
01:31Ferromagnetism
01:22MOSFET: Enhancement Mode
In their basic form, enhancement-mode MOSFETs are typically non-conductive when the gate-source voltage (Vgs) is zero. This default 'off' state means no...
01:16Biasing of P-N Junction
In equilibrium, no external voltage is applied across the p-n junction. The depletion region is formed at the junction interface due to the diffusion of carriers, which leaves behind charged dopants, acceptors on the p-side, and donors on the n-side. These immobile charges create an electric field that prevents further diffusion of carriers. The related energy band...
01:24Metal-Semiconductor Junctions
Schottky Barriers
Schottky barriers arise when a metal with a work function (Φm) contacts a semiconductor with a different work function (Φs). Initially, electrons transfer until the Fermi levels of the metal and semiconductor align at equilibrium. For instance, if Φm > Φs, the semiconductor Fermi level is higher than the metal's before contact. The...