Studies of Corrosion Inhibition Performance of Inorganic Inhibitors for Aluminum Alloy

In this study, the behavior of sodium silicate (Na₂SiO₃), manganese sulfate monohydrate (MnSO₄·H₂O), and ammonium metavanadate (NH₄VO₃) as corrosion inhibitors for AA6061 aluminum alloy (Al) was investigated. The polarization resistance (R_p) of the Al substrate immersed in 0.1 M NaCl solution was found to be 13 kΩ·cm². In comparison, the R_p of the Al substrate immersed in 0.1 M NaCl in the presence of Na₂SiO₃, Na₂SiO₃/MnSO₄·H₂O, and Na₂SiO₃/NH₄VO₃ inhibitors was found to be 100, 133, and 679 kΩ·cm², respectively. The best inhibition result was obtained when the mixture of the inhibitors was used with R_p of 722 kΩ·cm². The maximum percentage of the corroded area calculated from the scanning electron microscopy (SEM) images was found to be 5.7% for Al substrate immersed in 0.1 M NaCl, which decreased to 0.06% when the mixture of the inhibitors was used. The synergetic effects between the three inhibitors were studied, and the results illustrated that the combination of Na₂SiO₃, MnSO₄·H₂O, and NH₄VO₃ provided the best corrosion inhibition properties for Al in aqueous NaCl environments.