Photoluminescence and Stability of Dion-Jacobson Tin-Based Halide Perovskites with Different Spacer Cation Chain...

Two-dimensional tin halide perovskites are of significant interest for light emitting applications. Here, we investigate the effect of organic cation A on the stability of different Dion-Jacobson tin-based halide perovskites. The ASnBr₄ materials using diammonium cation A with shorter alkyl chains are found to exhibit improved stability, exhibiting dramatic stability difference between the most stable HDASnBr₄, where HDA denotes 1,6-hexanediammonium, and two materials with 8- and 10-carbon alkyl chain ammonium cations. The HDASnBr₄ powders were thermally stable at 100 °C in an argon environment but exhibited decreasing photoluminescence with time in ambient air at 100 °C. The sample degradation at 100 °C is accelerated compared to room temperature, but it proceeds along similar pathways, namely phase transformation followed by perovskite decomposition. Light emission from HDASnBr₄ thin films could be further enhanced by methanol vapor treatment, and warm white emission with Commission Internationale de l'Eclairage (CIE) coordinates (0.37, 0.34) could be obtained by combining HDASnBr₄ with a blue-emitting polymer film, while direct mixing of blue phosphor and HDASnBr₄ powder yields white emission with CIE coordinates of (0.34, 0.32).