Glasses for bone regeneration: structural features controlling physical properties and ion release of bioactive...

The structure, i.e. atomic arrangement, of glasses is known to determine many of their properties. This study investigates the structure of three well-known bioactive glass compositions, 45S5 (known as Bioglass), S53P4 (commercialised as BonAlive) and 13-93 (developed for improved high-temperature processing) by Si-29 and P-31 solid-state nuclear magnetic resonance and Raman spectroscopy. Results show that 45S5 has a more depolymerised silicate structure than the other two glasses, in agreement with its lowest silica content. These structural differences explain the well known high solubility and fast reactivity in vivo of 45S5 compared to the other two compositions. Differences between S53P4 and 13-93, by contrast, originate more from differences in their average modifier field strength, as their network connectivity, i.e. average silicate network polymerisation, is similar. As a result, 13-93 shows the lowest crystallisation tendency of the three glasses but also reacts relatively slowly during contact with aqueous solutions. The structural differences are also reflected in glass viscosity, where at a given temperature 45S5 has the lowest viscosity, 13-93 the highest and S53P4's viscosity is lying in between.