Kinetics of Precipitation Hardening Phases in Recycled 2017A Aluminum Alloy
Grażyna Mrówka-Nowotnik1, Grzegorz Boczkal2, Damian Nabel1
1Department of Material Science, Rzeszow University of Technology, Al. Powstancow Warszawy 12, 35-959 Rzeszow, Poland.
Abstract:
This study investigated the effect of the recycling process on the microstructure, hardness, and precipitation kinetics of strengthening phases in the 2017A aluminum alloy. Light microscopy (LM) and X-ray diffraction (XRD) analyses revealed that the as-cast microstructure of the recycled 2017A alloy contained intermetallic phases, including θ-Al2Cu, β-Mg2Si, Al7Cu2Fe, Q-Al4Cu2Mg8Si7, and α-Al15(FeMn)3(SiCu)2, and was comparable to that of the primary alloy, confirming its potential for high-performance applications. During solution heat treatment, most of the primary intermetallic precipitates, such as Al2Cu, Mg2Si, and Q-Al4Cu2Mg8Si7, dissolved into the solid Al matrix. DSC analysis of the solution-treated alloy established the precipitation sequence as follows: α-ss → GP/GPB zones → θ″ → θ'/Q' → θ-Al2Cu/Q-Al4Cu2Mg8Si7. The combined results from XRD, LM, TEM, and DSC confirmed that both θ and Q phases contributed to strengthening, with θ″ and θ' phases playing a dominant role. Brinell hardness measurements during natural and artificial aging revealed that hardness increased with aging time, reaching a maximum value of 150.5 HB after ~22 h of artificial aging at 175 °C. The precipitation kinetics of the recycled 2017A alloy was studied via DSC measurements over a temperature range of ~25 to 550 °C, at heating rates of 5, 10, 15, 20, and 25 °C/min. The peak temperatures of clusters, GP zones, and hardening phases (θ', θ″, θ, and Q) were analyzed to calculate the activation energy using mathematical models (Kissinger, Ozawa, and Boswell). The obtained values of activation energies of discontinuous precipitation were comparable across methods, with values for the θ″ phase of 89.94 kJ·mol-1 (Kissinger), 98.7 kJ·mol-1 (Ozawa), and 94.33 kJ·mol-1 (Boswell), while for the θ' phase, they were 72.5 kJ·mol-1 (Kissinger), 81.9 kJ·mol-1 (Ozawa), and 77.2 kJ·mol-1 (Boswell). These findings highlighted the feasibility of using recycled 2017A aluminum alloy for structural applications requiring high strength and durability.
More Related Videos
Related Concept Videos
Precipitation Processes
Washing, Drying, and Ignition of Precipitates
Precipitation Gravimetry
In determining nickel by gravimetric analysis, a precipitant of ethanolic dimethylglyoxime is added to a hot nickel salt solution. This is quickly followed by the dropwise addition of dilute ammonia solution until precipitation occurs. A...
Types of Coprecipitation
Sometimes, ions in a crystal lattice can undergo isomorphous replacement by inclusions of similar charge and size. For...
Recrystallization: Solid–Solution Equilibria
Precipitate Formation and Particle Size Control
The obtained precipitate should be either a pure substance of known composition or easily converted to one by a simple process, such as ignition or drying. In addition, the precipitate should be insoluble and easily filterable. In general, filterability...