Comparative Analysis of Spectral Broadening Techniques for Optical Temperature Sensing in Yttrium Fluoride (YF₃)...

In this work, YF₃:Nd³⁺ powder was synthesized using the microwave-assisted hydrothermal method at a low temperature (140 °C) and short synthesis time (1 h). The photoluminescence and optical temperature sensing properties of YF₃:Nd³⁺ were examined using 800 nm laser excitation, focusing on the emission corresponding to the ⁴F_3/2 → ⁴I_9/2 transition of Nd³⁺. The performance of YF₃:Nd³⁺ as an optical temperature sensor was evaluated using the full width at half maximum (FWHM), band broadening at 30% of maximum intensity (Δλ_30%), and valley-to-peak intensity ratio (VPR) techniques. All techniques demonstrated good repeatability and reproducibility. The best results were obtained using the VPR (V1/P1) method, which exhibited the highest relative sensitivity and the lowest temperature uncertainty, with values of 0.69 ± 0.02% K^-1 and 0.46 ± 0.09 K at 303 K, respectively. YF₃:Nd³⁺ shows promise as an optical temperature sensor operating entirely within the first biological window.