Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material
Published on: December 20, 2024
Wear behavior of 3D printed, minimally invasive restorations: Clinical data after 24 months in function
Magda Doumit1, Florian Beuer2, Mats Wernfried Heinrich Böse3
1Doctoral student, Department of Prosthodontics, Geriatric Dentistry and Craniomandibular Disorders, Charité-Universitätsmedizin Berlin, corporate member of Freie Universität Berlin and Humboldt-Universität zu Berlin, Berlin, Germany.
Statement Of Problem:
The prevalence of pathological tooth wear and a reduced vertical dimension of occlusion has increased, but prosthetic rehabilitation concepts have been invasive, time-consuming, and expensive. How affordable, esthetic, and less invasive treatment concepts will perform remains unclear.
Purpose:
The purpose of this proof-of-concept clinical study was to evaluate the wear behavior of 3-dimensionally (3D) printed, minimally invasive restorations fabricated from a ceramic- reinforced composite resin material after 24 months in clinical function.
Material And Methods:
The study included 28 participants who received noninvasive 3D printed restorations made of a computer-aided design and computer aided-manufacturing (CAD-CAM) ceramic-reinforced composite resin material (n=352). Maximum occlusal height loss and mean profile loss were measured by using an intraoral scanner and a matching software program (Geomagic Control X; 3D systems) by 1 clinician. Scans were conducted at baseline and after 12 and 24 months. A descriptive statistical analysis, including mean values, medians, standard deviations (SDs) interquartile range and 95% confidence interval (95% CI) were conducted (α=.05).
Results:
Maximum occlusal height loss and mean profile loss were analyzed. The molar restorations showed the highest mean values of maximum occlusal height loss after 12 (0.76 mm) and 24 (1.25 mm) months. The anterior restorations showed the lowest wear rates. In general, 123 restorations (35%) had material wear >0.5 mm and were classified as fractured after 24 months of clinical application. Most of the nonfractured restorations experienced localized material wear between 0.11 mm and 0.35 mm, whereas mean profile loss values varied between 0.05 mm and 0.11 mm.
Conclusions:
Three-dimensionally printed, noninvasive restorations manufactured from a ceramic-reinforced composite resin material showed considerable material wear after 2 years of clinical function, and the material appears suitable only for interim restorations.