Extending Interfaces in 3D to Achieve Superior Nanoscale Strength in Ti/Nb Nanolaminates

Tuning the atomic-level structure of nanolaminates enables high strength, increased deformability, and the ability to absorb and mitigate damage due to varied crystalline defects, including dislocations. We present the enhanced strength of Ti/Nb nanolaminates containing thick 3D interfaces (3DIs), relative to their chemically abrupt 2D counterparts. We examine the effects of crystallographic alignment and compositional gradients on mechanical behavior via experiments and phase-field-dislocation dynamics (PFDD) modeling. Mechanical testing reveals that nanolaminates containing thicker 3DIs demonstrate a 28% hardness enhancement compared with sharp-interface nanolaminates. PFDD modeling shows that the critical resolved shear stress (CRSS) increases with the 3DI thickness. Gradual compositional transitions in 3DIs were confirmed via scanning transmission electron microscopy and high-resolution transmission electron microscopy, showing sharp crystallographic transitions and a heightened interface topography. The findings establish a positive function between the 3DI thickness and mechanical robustness for hexagonal-closest-packed-containing composites, emphasizing the role of defect-interface interactions in tailoring the mechanical performance and providing a foundation for future interfacial engineering.