Evolutions in Microstructure and Mechanical Properties of Ultra-Thin Oligocrystalline Invar Alloy Strip During Cold...

The ultra-thin Invar alloy strips are widely used in the manufacture of the fine masks; cold rolling of such thin strips (<100 μm) poses significant difficulties, primarily due to the limited number of grains within the thickness range. Consequently, it is important to understand the grain structure and property evolutions of the ultra-thin Invar alloy strips during cold rolling. In this study, an annealed Invar36 alloy strip, 100 µm thick, was cold rolled to different thicknesses, and the surface deformation morphologies, cross-sectional grain structure, intracrystalline microstructure and tensile properties of these thin strips were characterized and analyzed. The results show that plastic deformation of the initial annealed equiaxed grains is not uniform, depending on the grain orientation, resulting in different slip bands morphologies, unevenness and increase in roughness. Meanwhile, the grain rotation and rolling texture develop with increasing cold rolling reduction. The dislocation density in the 60% cold-rolled strip is about decuple that of the original annealed strip, and high-density tangled dislocations are formed, making the tensile strength increase from 430 MPa to 738 MPa. Grain refining and proper intermediate annealing are proposed to optimize the thickness uniformity, evenness and surface roughness.