Effect of Hot Isostatic Pressure on the Microstructure Evolution of Ti-22Al-25Nb Alloy Formed by Selective Laser...

The density of SLMed (Selective Laser Melting) Ti-22Al-25Nb alloy was improved through hot isostatic pressing (HIP) treatment, and the influence of HIP and solution aging on the microstructure of Ti-22Al-25Nb alloy in the as-deposited state was examined. The results indicate that following (1100 °C + 300 MPa)/3 h-HIP, the specimen densities have risen to 99.71%, porosity has markedly decreased, and internal flaws have been eradicated. Microstructural analysis reveals a significant presence of GBα₂ (GB, Grain Boundary) along grain boundaries, with GBLO + α₂ (GBL, Grain Boundary Lath; O, Orthorhombic) laths extending parallel from the grain boundaries into the intragranular region. Additionally, a limited number of cross or snowflake O + α₂ lath clusters and acicular O phases are precipitated within the B2 (B, Body-centered cubic) phase in the HIPed state, characterized by isotropic and linear grain boundaries. The GBLα₂ and GBLO exhibit two growth modes: sympathetic nucleation and interfacially unstable nucleation. During the solid solution treatment following HIP, as the solid solution temperature rises, the acicular O phase, GBLO, lath O phase, lath α_2, and GBα₂ sequentially dissolve, increasing the volume fraction of the B2 phase. After HIP, the aging microstructure is primarily characterized by the proliferation of the acicular O phase precipitated from the B2 phase and retaining the lath O phase in a solid solution. The precipitation of GBLO in the original solid solution is suppressed, and the GBLα₂ in the original solid solution partially decomposes into rimO, resulting in coarse grain size and significant internal decomposition of α₂. Following solution treatment and aging at 920 °C, the proliferation of the acicular O phase enhances ductility, resulting in ideal overall characteristics with a yield strength (YS) of 760.81 MPa, ultimate tensile strength (UTS) of 869.32 MPa, and elongation (EL) of 2.683%. This study demonstrates that the HIP treatment and the modification of solution aging parameters can substantially increase the density and refine the microstructure of Ti-22Al-25Nb alloy, hence enhancing its mechanical properties.