Synchrotron X-ray photoelectron spectroscopy study of sodium adsorption on vertically arranged MoS₂ layers coated...

Hybrid materials consisting of molybdenum disulfide (MoS₂) and graphitic-like carbon have great potential for practical application as anodes in high-performance sodium-ion batteries. In this work, to reveal the effect of carbon coating on the interaction of sodium with the MoS₂ layers located vertically relative to the substrate, model experiments were carried out using synchrotron-radiation-induced X-ray photoelectron spectroscopy (XPS). Sodium vapor obtained by heating a sodium source was simultaneously deposited in vacuum on the surfaces of MoS₂, pyrolytic carbon, and a hybrid sample obtained by transferring a pyrolytic carbon film onto the MoS₂ film. According to XPS data, sodium easily penetrates into the space between the vertical layers of the uncoated film, and its interaction with MoS₂ leads to the transformation of the original hexagonal structure into a distorted tetragonal one. Under the experimental conditions, sodium is unable to diffuse through the carbon film consisting of horizontally oriented graphene domains and is almost completely removed by annealing the sample at 773 K in ultrahigh vacuum. The presence of the underlying MoS₂ film facilitates the diffusion of sodium through the graphitic coating, but not all of the deposited sodium reaches MoS₂. As a result, the sodium-induced rearrangement of the carbon-coated MoS₂ is less than that of the free MoS₂ film, and annealing of the sodiated sample restores its structure. The obtained results demonstrate the important role of the graphitic coating in the development of viable MoS₂-based electrodes for energy storage systems.