Design and Synthesis of Fe₃O₄-Loaded Polymer Microspheres with Controlled Morphology: Section II Fabrication of...

A simple and innovative synthesis strategy was established to produce polymer microspheres with a distinctive walnut-like morphology, incorporating Fe₃O₄ nanoparticles within their structure. This was achieved through γ-ray-initiated mini-emulsion polymerization. To ensure high encapsulation efficiency, the surface of the Fe₃O₄ nanoparticles was chemically altered to shift their wettability from hydrophilic to hydrophobic, enabling uniform dispersion within the monomer phase before polymerization. The formation of the walnut-like architecture was found to be significantly influenced by both the polymerization dynamics and phase separation, as well as the shrinkage of the crosslinked polymer network formed between the monomer and the resulting polymer. Divinylbenzene (DVB) was chosen as the monomer due to its ability to generate a mechanically stable polymer framework. The γ-ray irradiation effectively initiated polymerization while preserving structural coherence. A detailed analysis using FTIR, SEM, and TEM confirmed the successful fabrication of the Fe₃O₄-loaded polymer microspheres with their characteristic textured surface. Moreover, magnetic characterization via vibrating sample magnetometry (VSM) indicated pronounced superparamagnetic behavior and strong magnetic responsiveness, highlighting the potential of these microspheres for advanced biomedical applications.