Insights into the Crystal Structure and Magnetodielectric Properties of High-Energy Ball Milled Sr Substituted LaFeO₃

The effect of strontium substitution on the crystal tructure, as well as the magnetic, and electrical properties of lanthanum ferrite (LaFeO₃) synthesized by high-energy ball milling, is studied, with an emphasis on magnetodielectric coupling. X-ray diffraction (XRD) confirmed the successful synthesis of orthorhombic La_1-xSr_xFeO₃ for doping levels up to 0.2 mol. At 0.3 mol Sr²⁺, two phases appear: La_0.6Sr_0.4FeO_2.976 and La_0.8Sr_1.2FeO_3.714, the latter being metastable. This phase vanishes at 0.5 mol. The Fourier Transform Infrared Spectroscopy (FT-IR) and Scanning Electron Microscopy coupled with Energy Dispersive X-ray Spectroscopy (SEM-EDS) analysis confirmed these results using a vibrating sample magnetometer (VSM), whose measurements show ferromagnetism at 0.1 and 0.3 mol Sr²⁺, attributed to crystal distortion, magnetic spin rearrangement, and as consequence, modifications in the double-exchange interactions. Dielectric tests reveal that higher Sr²⁺ concentrations lead to increased relative permittivity, dielectric losses, and conductivity, linked to oxygen vacancy formation. This study demonstrates a room-temperature magnetodielectric coupling of 32% in Sr-doped lanthanum ferrite, highlighting its potential for technological applications.