Durability Assessment of Alkali-Activated Geopolymers Matrices for Organic Liquid Waste Immobilization

Rosa Lo Frano1, Salvatore Angelo Cancemi1, Eleonora Stefanelli1

  • 1Dipartimento di Ingegneria Civile e Industriale, Università di Pisa, Largo Lucio Lazzarino 2, 56122 Pisa, Italy.

Materials (Basel, Switzerland)
|July 12, 2025
PubMed

Keywords:
fire resistancegeopolymerliquid organic wasteradioactive waste managementthermal ageing

More Related Videos

Extraction of Structural Extracellular Polymeric Substances from Aerobic Granular Sludge06:10

Extraction of Structural Extracellular Polymeric Substances from Aerobic Granular Sludge

Published on: September 26, 2016

23.0K
Synthesis of Thermogelling PolyN-isopropylacrylamide-graft-chondroitin Sulfate Composites with Alginate Microparticles for Tissue Engineering12:22

Synthesis of Thermogelling PolyN-isopropylacrylamide-graft-chondroitin Sulfate Composites with Alginate Microparticles for Tissue Engineering

Published on: October 26, 2016

12.0K

Related Concept Videos

Alkali Aggregate Reaction in Concrete01:26

Alkali Aggregate Reaction in Concrete

The alkali-aggregate reaction in concrete involves natural siliceous minerals in aggregates reacting with alkaline hydroxides derived from cement alkalis. This reaction forms an alkali-silica gel that absorbs water, swells, and increases in volume, which is confined by the surrounding cement paste, creating internal pressures that crack and disrupt the concrete. The extent of expansion and damage can be partly attributed to the alkali-silica reaction's osmotic hydraulic pressure and the...
190
Mortar Properties01:17

Mortar Properties

Mortar properties encompass a range of characteristics crucial for construction and masonry work, including workability, water retention, bond strength, durability, compressive strength, volume change, and appearance. Workability refers to mortar's ability to be easily applied and manipulated without sagging or falling off surfaces, which is important for efficient masonry unit placement and alignment. Water retention is essential to prevent the mortar from losing moisture too quickly to...
189
Testing Water Quality01:14

Testing Water Quality

When the quality of water for concrete preparation is uncertain, its impact on the setting time of cement and compressive strength of mortar is assessed by comparison with de-ionized or distilled water benchmarks. American Society for Testing and Materials (ASTM) C1602 requires the setting times to be within 90 minutes of the control, British Standard (BS) 3146:1980 allows a 30-minute variance in the initial setting, while British Standards European Norm (BS EN) 1008 specifies initial setting...
189
Waterproofing and Anti-Bacterial Admixtures in Concrete01:22

Waterproofing and Anti-Bacterial Admixtures in Concrete

Concrete's susceptibility to water absorption is due to the capillary action within the pores of its hydrated cement paste. This action draws water in, creating the need for waterproofing admixtures to prevent such penetration. The efficacy of these admixtures is contingent upon the water pressure, with variations arising from different conditions such as rain, capillary rise, or hydrostatic pressure in structures intended to hold water.
Waterproofing admixtures render concrete hydrophobic,...
113