Evaluation of Shear Bond Strength in the Repair of Additively and Subtractively Manufactured CAD/CAM Materials Using...

Biomimetic restorative protocols aim to preserve natural tooth structure while enhancing restoration longevity. This in vitro study aimed to evaluate the shear bond strength (SBS) in the repair of additively and subtractively manufactured CAD/CAM materials using bulk-fill resin composites and to assess the effect of thermocycling. Forty rectangular specimens (14.5 × 7 × 3 mm) were prepared from Grandio Blocs (GB, VOCO) and VarseoSmile Crown^Plus (VS, BEGO), and thermocycled (5000 cycles, 5-55 °C, 20 s dwell time). All surfaces were roughened with 50 μm Al₂O₃. Samples were repaired using VisCalor (VCB, VOCO) and Charisma Bulk Flow One (CBO, Kulzer) composites (n = 10 per group) with their respective adhesives. Each group was further divided into immediate and post-thermocycling subgroups. All specimens were tested under shear force until failure, and failure types were examined under a stereomicroscope. Representative samples were examined by SEM to evaluate filler morphology. Statistical analysis was performed with SPSS v23 (p < 0.05). No statistically significant differences in SBS were found between groups (p > 0.05). Mean SBS values were highest in VS-CBO and lowest in GB-CBO. Cohesive failures were more frequent in immediate groups, while adhesive failures predominated after thermocycling. Bulk-fill composites did not influence the repair bond strength of indirect materials. Thermocycling affected the failure type, though not the SBS values.