Binder-Free Fe₂O₃/MWCNT/Al Electrodes for Supercapacitors

This work presents a method for preparing an Fe₂O₃/MWCNT/Al composite electrode without the use of a binder. Synthesizing the composite material directly on conductive substrates allows one to obtain ready-made supercapacitor electrodes characterized by high values of specific capacity, as well as resistance to numerous charge/discharge cycles. Using an array of multi-walled carbon nanotubes (MWCNTs) as a conductive base for the synthesis of iron oxide allows for the production of a composite material that combines the positive properties of both materials. The Fe₂O₃/MWCNT/Al composite was formed using electrochemical oxidation of the MWCNT/Al material in a mixture of 0.1 M aqueous solution of Fe(NH₄)₂(SO₄)₂ (iron ammonium sulfate) and 0.08 M CH₃COONa (sodium acetate) in a 1:1 ratio. The proposed approaches to fabricating composite electrodes provide excellent performance characteristics, namely high cyclic stability and fast response time. For the first time, an Fe₂O₃/MWCNT/Al composite was obtained using electrochemical oxidation of Fe²⁺ on the surface of MWCNTs grown directly on aluminum foil. The specific capacitance of the obtained composite material reaches 175 F/g at a scanning rate of 100 mV/s. The capacity loss during cyclic measurements does not exceed 25% after 10,000 charge/discharge cycles.