Tuning of Photocatalytic and Piezophotocatalytic Activity of Bi₃TiNbO₉ via Synthesis-Controlled Surface Defect...

In this work, we investigate advanced photocatalyst Bi₃TiNbO₉ as promising piezophotocatalyst in terms of the effect of synthesis methods on the surface chemistry, structure, and catalytic performance in process of contaminant removal. Samples were prepared via solid-state reaction (BTNO-900) and molten salt synthesis (BTNO-800), leading to distinct morphologies and defect distributions. SEM imaging revealed that BTNO-900 consists of agglomerated, irregular particles, while BTNO-800 exhibits well-faceted, plate-like grains. Nitrogen adsorption analysis showed that the molten-synthesized sample possesses a significantly higher specific surface area (5.9 m²/g vs. 1.4 m²/g) and slightly larger average pore diameter (2.8 nm vs. 2.6 nm). High-resolution XPS revealed systematic shifts in binding energies for Bi 4f, Ti 2p, Nb 3d, and O 1s peaks in BTNO-900, accompanied by a higher content of adsorbed oxygen species (57% vs. 7.2%), indicating an increased concentration of oxygen vacancies and surface hydroxylation due to the solid-state synthesis route. Catalytic testing demonstrated that BTNO exhibits enhanced piezocatalytic efficiency of Methylene Blue degradation (~78% for both samples), whereas BTNO-800 shows significantly reduced photocatalytic activity (45.6%) compared to BTNO-900 (84.1%), suggesting recombination effects dominate in the more defective material. Synergism of light and mechanical stress results in piezophotocatalytic degradation for both samples (92.4% and 93.4%, relatively). These findings confirm that synthesis-controlled defect engineering is a key parameter for optimizing the photocatalytic behavior of Bi₃TiNbO₉-based layered oxides and crucial role of its piezocatalytic activity.