Structural Stability and Kinetics of Hydrogenation of β‑Tantalum at Low Temperatures

The development of reliable hydrogen sensing materials for subzero environments is crucial for aviation, cryogenic storage, and hydrogen infrastructure applications. In this study, we investigate tetragonal β-tantalum (β-Ta) thin films at -60 °C to assess their potential for optical hydrogen sensing. In situ X-ray diffraction (XRD) measurements reveal a reversible lattice expansion upon hydrogen exposure, with β-Ta exhibiting a smaller volumetric expansion compared to α-Ta, indicating lower hydrogen solubility. Optical transmission measurements demonstrate a monotonic and fully reversible optical response across a range of hydrogen pressures, free of any hysteresis. However, β-Ta exhibits prolonged response times at low temperatures due to diffusion-limited kinetics, as confirmed by power-law response rate analysis and direct diffusion front measurements. Although β-Ta offers a temperature-independent resolution and structural robustness, its slower response time suggests the need for further microstructural optimizations to enhance hydrogen diffusion.