Wet Spun Aramid Nanofiber-Templated Hybrid Hydrogel Desiccant Filaments for Atmospheric Water Harvesting

Atmospheric water vapor is an abundant and renewable resource that can alleviate growing water scarcity. Hybrid hydrogel desiccants composed of hygroscopic salts hold significant promise for atmospheric water harvesting (AWH) due to their increased capacity for water uptake. Thus far, many efforts in fabricating these desiccants require multistep processes, where the salt impregnation is achieved post-hydrogel fabrication. Here, we develop a scalable wet spinning methodology using aramid nanofibers (ANFs) to template and coagulate hydroxypropyl cellulose (HPC) into filaments in a coagulation bath consisting of water and lithium chloride (LiCl). HPC serves as the matrix to retain the captured water vapor, and later releases it upon heating. ANFs serve as the physical cross-linker between HPC, allowing for wet spinning at a speed up to 61 m h^-1. The composite filaments achieve up to 0.55 g g^-1 water uptake at 30% relative humidity (RH) and 21 °C, reaching 80% saturation in 40 min. With a lower critical solution temperature of 39 °C, the desiccant filaments can release up to 72% of the captured water at 60 °C after 30 min. In an AWH chamber, the filaments can achieve daily water production of 5.21 L kg^-1 day^-1 at 30% RH and 21 °C.