Dialdehyde Cellulose Nanocrystals and Proanthocyanidins Reinforced Soy Protein Isolate Films for Blueberry...

Exhibiting significant potential for sustainable packaging due to their renewability and biodegradability, soy protein isolate (SPI) films are nevertheless critically hampered by inherent brittleness, poor water resistance, and a lack of bioactivity. Herein, we demonstrate a hierarchical multi-network strategy that transforms SPI into a high-performance, functional biocomposite. A robust covalent backbone was forged via Schiff base cross-linking between SPI and dialdehyde cellulose nanocrystals (DACNCs) derived from agricultural biomass, while proanthocyanidins (PAs) were strategically incorporated to create a secondary, pervasive hydrogen-bonding network. This hierarchical architecture effectively overcomes the typical trade-offs between mechanical strength and functionality seen in singly modified biopolymers, unlocking a suite of remarkable performance enhancements. The optimized film exhibited a 491% increase in tensile strength (to 15.54 MPa) and elevated thermal stability to 330 °C. Critically, the film was endowed with potent functionalities, including complete UV-blocking, high antioxidant capacity (93.2% ABTS scavenging), and strong, broad-spectrum antimicrobial activity. The film's practical efficacy was validated in a preservation test, where the coating extended blueberry shelf life by inhibiting fungal spoilage and reducing weight loss by nearly 30% relative to uncoated controls after 15 days of storage. This work provides a powerful framework for developing advanced biocomposites with tailored properties for active food packaging and beyond.