This study investigates the development of biodegradable, scented bio-composite filaments incorporating industrial residues, specifically spent coffee grounds (SCG) and lignin (LI), into a PLA matrix for FDM 3D printing. Two fragrance additives, essential oil (EO) and microencapsulated fragrance powder (FP), were introduced (3%) to enhance sensory properties. The research investigates the effects of filler content (5%, 10%, and 15%) and fragrance additives on the surface chemistry (FTIR), thermal stability (TGA and DSC), mechanical properties (Tensile, flexural and impact), microstructure, and dimensional stability (Water absorption test and thickness swelling). Incorporating industrial residues and additives into PLA reduced the thermal stability, the degradation temperature and the glass transition temperature but increased the residual mass and the crystallinity. The effect of lignin was more pronounced than that of SCG, significantly influencing these thermal properties. Increasing the filler content of spent coffee grounds and lignin also led to a progressive decrease in tensile, flexural, and impact strength due to poor interfacial adhesion and increased void formation. However, lignin-based biocomposites exhibited enhanced stiffness at lower concentrations (≤10%), while biocomposites containing 15% SCG doubled their elongation at break compared to pure PLA. Adding fragrance reduced the mechanical strength but improved ductility due to plasticizer-like interactions. Microstructural analysis revealed heterogeneity in the biocomposites' fracture surface characterized by the presence of pores, filler agglomeration, and delamination, indicating uneven filler dispersion and limited interfacial adhesion, particularly at high filler concentrations. The water absorption and dimensional stability of 3D-printed biocomposites increased progressively with the addition of residues. The presence of essential oil slightly improved water resistance by forming hydrogen bonds that limited moisture absorption. This article adds significant value by extending the potential applications of biocomposites beyond conventional engineering uses, making them particularly suitable for the fashion and design sectors, where multi-sensory and sustainable materials are increasingly sought after.