Laser Remelting of Biocompatible Ti-Based Glass-Forming Alloys: Microstructure, Mechanical Properties, and...

Titanium-based bulk metallic glasses (BMGs) offer high strength, lower stiffness than Ti-6Al-4V, and superior corrosion resistance, but conventional Ti glass-forming systems often contain toxic Ni, Be, or Cu. This work investigates five novel Ti-based alloys free of these elements-Ti₄₂Zr₃₅Si₅Co_12.5Sn_2.5Ta₃, Ti₄₂Zr₄₀Ta₃Si₁₅, Ti₆₀Nb₁₅Zr₁₀Si₁₅, Ti₃₉Zr₃₂Si₂₉, and Ti_65.5Fe_22.5Si₁₂-synthesized by arc melting and suction casting. Single-track laser remelting using a selective laser melting (SLM) system was performed to simulate additive manufacturing and examine microstructural evolution, cracking behavior, mechanical properties, and cytocompatibility. All alloys solidified into fully crystalline α/β-Ti matrices with Ti/Zr silicides; no amorphous structures were obtained. Laser remelting refined the microstructure but did not induce glass formation, consistent with the known limited glass-forming ability of Cu/Ni/Be-free Ti systems. Cracking was observed at low laser energies but crack density decreased as laser energy increased. Cracks were eliminated above ~0.4 J/mm for most alloys. Ti₄₂Zr₃₅Si₅Co_12.5Sn_2.5Ta₃ exhibited the lowest stiffness (~125 GPa), while Ti₆₀Nb₁₅Zr₁₀Si₁₅ showed the highest due to silicide precipitation. Cytotoxicity tests (ISO 10993-5) confirmed all alloys to be non-toxic, with some extracts even enhancing fibroblast proliferation. This rapid laser-remelting approach enables cost-effective screening of Ti-based glass-forming alloys for additive manufacturing. Ti-Zr-Ta-Si systems demonstrated the most promising properties for further testing using the powder bed method.