Surface Engineering of Non-Equiatomic TiZrNbTaMo HEA by MAO Treatment in a Cu-Rich Electrolyte for Biomedical...

This study evaluated the surface functionalization of a non-equiatomic TiZrNbTaMo high-entropy alloy (HEA) by micro-arc oxidation (MAO) in Cu-rich electrolytes to tailor its performance for biomedical implants. The Cu content was varied, and the resulting coatings were investigated for their morphology, phase constitution, chemical structure, wettability, and cytocompatibility. X-ray diffraction (XRD) measurements of the substrate indicated a body-centered cubic (BCC) matrix with minor HCP features, while the MAO-treated samples depicted amorphous halo with sparse reflections assignable to CaCO₃, CaO, and CaPO₄. Chemical spectroscopic analyses identified the presence of stable oxides (TiO₂, ZrO₂, Nb₂O₅, Ta₂O₅, MoO₃) and the successful incorporation of bioactive elements (Ca, P, Mg) together with traces of Cu, mainly as Cu₂O. MAO treatment increased surface roughness and rendered a hydrophilic behavior, which are features typically favorable to osseointegration process. In vitro cytotoxic assays with MC3T3-E1 cells (24 h) showed that Cu addition did not induce harmful effects, maintaining or improving cell viability and adhesion compared to the controls. Collectively, MAO in Cu-rich electrolyte yielded porous, bioactive, and Cu-incorporated oxide coatings on TiZrNbTaMo HEA, preserving cytocompatibility and supporting their potential for biomedical applications like orthopedic implants and bone-fixation devices.