Bond strength of thermoformed and 3D-printed aligners with universal primer versus one-step aligner adhesive with and
Viet Anh Nguyen1, Viet Hoang2, Thi Quynh Trang Vuong3
1Department of Orthodontics, Faculty of Dentistry, Phenikaa University, Hanoi, Viet Nam.
Objectives:
Chairside bonding of auxiliaries directly to aligners can avoid remanufacturing trays, but optimal protocols may be substrate-specific across modern thermoformed and 3D-printed materials. This study aimed to compare bond strength and failure mode across six representative aligner materials using a universal primer-orthodontic adhesive combination and a one-step aligner adhesive, with and without sandblasting.
Materials And Methods:
Polyethylene terephthalate glycol-modified (PETG), thermoplastic polyurethane (TPU), and glycol-modified polycyclohexylenedimethylene terephthalate (PCTG), together with three 3D-printed resins (TA-28, TC-85DAC, DCA), were prepared as 0.76-mm plates (n = 64). Specimens received alumina sandblasting or no treatment, then were bonded with either of two bonding strategies (n = 16). After thermocycling, bond strength was tested, and failures were scored by ARI. Two- and three-way ANOVA and proportional-odds modeling assessed effects (α = 0.05).
Results:
Bond strength showed significant main effects of material and sandblasting, with significant material-sandblasting and material-primer interactions. The primer main effect was not significant. Post hoc tests confirmed substrate-specific rankings. PETG with Bond Aligner (non-sandblasted) reached 26.71 MPa, while DCA with universal primer (sandblasted) reached 22.36 MPa. Sandblasting generally increased bond strength, with some exceptions. Failure mode was material-dependent and not completely parallel with bond strength.
Conclusions:
Bonding efficacy depends on the aligner substrate. For thermoformed trays, a one-step aligner adhesive is preferable, with sandblasting contraindicated for PETG but advantageous for more elastic TPU and PCTG. For 3D-printed trays, a universal primer-orthodontic adhesive combination performs more consistently, with sandblasting benefiting DCA and TA-28, whereas TC-85DAC performs slightly better without it.
Related Concept Videos
01:12Bonding and Strength of Aggregate
01:17Design Example: Alignment of a Road Line Using GIS
01:29Impression Management Techniques III: Aligning Actions
02:49Bond Energies and Bond Lengths
00:42Ionic Bonds
When atoms gain or lose electrons to achieve a more stable electron configuration they form ions. Ionic bonds are electrostatic attractions between ions with opposite charges. Ionic compounds are rigid and brittle when solid and may dissociate into their constituent ions in water. Covalent compounds, by contrast, remain intact unless a chemical reaction breaks them.
Opposing Charges Hold Ions Together in Ionic Compounds
Ionic bonds are reversible electrostatic interactions between ions...
03:05Acid Strength and Molecular Structure
In the absence of any leveling effect, the acid strength of binary compounds of hydrogen with nonmetals (A) increases as the H-A bond strength decreases down a group in the periodic table. For group 17, the order of increasing acidity is HF < HCl < HBr < HI. Likewise, for group 16, the order of increasing acid strength is H2O < H2S < H2Se < H2Te. Across a row in the periodic table, the acid strength of binary hydrogen compounds increases with increasing...