Synergistic Effect of Conditioned Medium and Calcium Phosphate Biocement on Osteogenic Properties of Composite

The aim of the study was to investigate the synergistic effect of conditioned medium (CM) and two types of calcium phosphate biocements on the osteogenic properties of a composite material through rat bone marrow-derived mesenchymal stem cells (MSCs). Briefly, MSCs were cultured for 7 and 17 days in extracts derived from the two biocement types. These extracts were supplemented with 5% (v/v) of concentrated CM. The CM was obtained from rat bone marrow MSC cultures after a 48 h conditioning period. The results showed that the addition of CM had a significant positive impact on the osteoblastic differentiation of MSCs, particularly in the extracts from the tetracalcium phosphate/monetite/calcium sulfate hemihydrate biocement (designated as CAS cement) compared to the other tested cement extract (designated C cement). After 17 days of culturing, a notable increase in cell viability and alkaline phosphatase (ALP) activity, as well as the upregulation of osteoblastic-related gene expression, was found. This enhancement in osteogenic activity was likely driven by the growth factors and bioactive molecules present in the CM. The study concluded that supplementing the biocement extracts with only 5% of 10X concentrated CM is sufficient to significantly influence and improve the in vitro characteristics, cell behavior, gene expression, and synthesis of cell products. It was demonstrated that, especially in the CAS supplemented with CM (CAS + CM) extract system, the improvement in osteogenic properties was due to the synergistic effect between the higher concentration of calcium ions in extracts released from the calcium sulfate hemihydrate-containing cement and the bioactive molecules supplied by the CM.