Unraveling In-Situ Formation of Surface Nickel Nitride Structures in Plasma-Assisted Catalytic Ammonia Synthesis

We report the in situ formation of Ni nitride for plasma-assisted ammonia synthesis. Both the surface nitrogen concentration and the ammonia formation rate exhibit dependence on the N₂:H₂ feed ratio. The maximum surface nitrogen concentration occurs at a N₂:H₂ ratio of 4:1, and the maximum catalytic activity occurs at 2:1. In contrast, the formation of gas phase radicals is less sensitive to feed composition, indicating that Ni nitride is more kinetically relevant to ammonia production than gas-phase radicals. The plasma-induced formation of Ni nitride is therefore proposed to be a critical contributor to the synergistic effects in plasma-assisted catalytic ammonia synthesis. Additionally, Ni nitride alters the surface reaction mechanism of plasma-assisted ammonia synthesis, with the rate-determining-step (RDS) shifting to surface-bound NH₃ formation rather than N₂ activation at temperatures below 373 K. These findings provide mechanistic insight that opens opportunities for optimizing the performance of plasma-assisted catalytic ammonia synthesis.