Cure Efficiency and Biocompatibility of an Iron-Based Coordination Complex as a Photoinitiator for Dental 3D-Printed
Sharanya Singh1, Mateus Garcia Rocha1, Mario Alexandre Coelho Sinhoreti2
1Department of Restorative Dental Sciences, Center for Dental Biomaterials, College of Dentistry, University of Florida, 1390 Center Drive, Gainesville, FL 32610, USA.
Objective:
The aim of this study was to evaluate the cure efficiency and biocompatibility of a novel iron-based coordination complex used as a photoinitiator in comparison to conventional ethyl (2,4,6-trimethylbenzoyl) phenylphosphinate (TPO-L) and camphorquinone (CQ) as photoinitiators in dental 3D-printed resins.
Materials And Methods:
Experimental dental resin formulations were prepared by blending 1:1 ratio of Bis-GMA and TEGDMA, to which 0.2 wt% of either the iron-based coordination complex or CQ were added, along with 0.2 wt% EDAB and 0.4 wt% IOD, and the TPO-L. The degree of conversion (DC) was measured using Fourier transform infrared spectroscopy (FTIR). Biocompatibility was assessed by evaluating the viability of L929 fibroblast-like cells using the MTT assay 24 h post-exposure. Statistical analyses included a two-way ANOVA followed by Tukey's test for post hoc comparisons, with significance at p < 0.05.
Results:
The degree of conversion for the iron-based coordination complex (84.54% ± 1.69%) was significantly higher than that for the TPO-L (78.77% ± 1.25%) and CQ-based resins (73.21% ± 0.47%) (p < 0.001). The iron-based coordination complex and TPO-L resins exhibited significantly higher conversion than CQ-based resins (p < 0.001). Regarding biocompatibility, the cell viability test revealed that the iron-based coordination complex demonstrated the highest cell viability at 86.5% ± 10.24%, followed by TPO-L with 80.03% ± 11.07%. CQ showed the lowest cell viability of 51.29% ± 8.44% (p < 0.05). Tukey's test confirmed significant differences between CQ and other photointiators (p < 0.05), while no significant difference was found between TPO-L and the iron-based coordination complex.
Conclusions:
This study introduces a novel iron-based coordination complex photoinitiator that demonstrates enhanced cure efficiency and comparable biocompatibility to TPO-L, while significantly reducing the cytotoxicity associated with CQ. Its longer absorption wavelength supports deeper layer curing, making it a promising alternative for dental 3D printing, particularly in bioactive scaffold applications requiring minimized cytotoxicity.