Leveraging Machine Learning for Screening Metal-Organic Frameworks with Selective CO₂ Recognition for Early Thermal...

The escalation of thermal runaway in lithium-ion batteries presents severe safety hazards that necessitate advanced monitoring protocols to ensure early warning of potential failures. Carbon dioxide (CO₂) is released during preliminary decomposition well before catastrophic failure occurs, thereby providing a strategic advantage for early-stage warning. Consequently, identifying materials with high-selective CO₂ recognition is an essential prerequisite for developing reliable sensing platforms. This study integrates Grand Canonical Monte Carlo simulations with Random Forest (RF) models to systematically screen 1470 MOFs from the CoRE-MOF 2019 database. The screening process evaluates selective CO₂ recognition under multicomponent competitive adsorption conditions involving CO₂, C₂H₄, and O₂. The performance evaluation is based on working capacity, selectivity, and the trade-off between working capacity and selectivity (TSN). The RF model achieves high predictive accuracy, with tested R² exceeding 0.92 on the test samples. Shapley Additive Explanations (SHAP) interpretability analysis identifies Q⁰_st(CO₂), Q⁰_st(C₂H₄), WEPA, K_H(C₂H₄), and ETR as key performance drivers. The results indicate that CO₂ selectivity is constrained by the binding strength of competing C₂H₄. Optimal materials tend to have hard Lewis acid centers and polar inorganic clusters to minimize non-specific π-interactions with interfering species. Top-performing MOFs require balanced structural features, concentrating in moderate surface areas (965-1975 m²/g), narrow pore windows (PLD ≈ 4-7 Å, LCD ≈ 5.5-9.6 Å), high void fractions above 0.6, and low densities below 1.3 g/cm³. AJOTEY emerges as the optimal candidate with a TSN of 6.43 mol/kg, combining substantial working capacity (4.57 mol/kg) with strong selectivity (25.52). These results will accelerate the discovery of sensing materials and provide a practical pathway for MOF-based CO₂ sensor development to enhance lithium-ion battery safety.