Predictions of Wear Performances of AlSi7Mg0.6 Cast Aluminum Alloy Under Different Displacement and Applied Load

AlSi7Mg0.6 aluminum alloy is widely adopted in many industrial fields due to its favorable mechanical properties and lightweight merits. In the catenary system of high-speed railways, AlSi7Mg0.6 aluminum alloy is adopted as the substrate of the positioning hook and positioning support, which exhibit abnormal wear in some railways. Thus, it is very important to reveal the underlying wear characteristics and discover the key factors involved. In this study, the influences of displacement (0.5 mm, 1.5 mm, and 3.0 mm) and applied load (20 N, 50 N, 100 N, and 200 N) on the wear performance of AlSi7Mg0.6 aluminum alloy are investigated experimentally and numerically. Wear experiments are time-consuming and costly, but the finite element method (FEM) can effectively solve this problem. A UMESHMOTION user-defined subroutine integrated with an ABAQUS Arbitrary Lagrangian-Eulerian (ALE) adaptive mesh technique was developed to simulate the wear evolution process of the aluminum alloy under varying displacements and applied loads. The results indicate that the wear evolution process of AlSi7Mg0.6 aluminum alloy can be effectively simulated using the UMESHMOTION subroutine. The maximum wear depth (MWD) from the FEM deviates from the experimental results by no more than 10%, and the deviation is smaller than the experimental values. The largest deviation occurs when the displacement is 3.0 mm and the applied load is 100 N, where the discrepancy reaches 7.53%. The wear volume (WV) obtained from the FEM shows a deviation of less than 20% compared to experimental results. For the case with a displacement of 0.5 mm, the numerical results underestimate the wear volume, while for the case with displacements of 1.5 mm and 3.0 mm, the numerical results overestimate the wear volume. The largest deviation in this case occurs for the case with a displacement of 3.0 mm and applied loading of 100 N, with a discrepancy of 16.33%.