Structural, Thermal Behaviour and Tribological Performance in Cold Rolling of Mineral Lubricants with Graphene...

In this study, nanolubricants based on SAE 5W-30 mineral oil were formulated using oleic acid-functionalized graphene nanoplatelets (GNPs), and their colloidal stability, rheological behaviour, thermal stability, and tribological performance under cold rolling conditions were systematically investigated. The nanolubricants were prepared at GNP concentrations of 0.05, 0.1, 0.2, 0.4, and 0.6 wt%. FT-IR analysis confirmed successful functionalization, evidenced by the characteristic C=O band at approximately 1710 cm^-1 and changes in CH₂ stretching vibrations in the 2850-3000 cm^-1 range. UV-VIS results indicated initially homogeneous dispersions; however, after three days, relative concentrations decreased to 95%, 90%, and 75% for 0.05, 0.2, and 0.6 wt% GNPs, respectively. Viscosity measurements showed minimal variation at low concentrations, with only a 0.64% increase at 0.2 wt% compared to the base oil. TGA revealed enhanced oxidative stability at low GNP contents, with the oxidation onset temperature increasing from 205.3 °C to 207.2 °C at 0.05 wt%, while a marked decline was observed at higher concentrations (176.8 °C at 0.6 wt%). In cold rolling experiments at a 3% reduction ratio, the rolling force was measured at 1341 N/mm with the neat lubricant, decreasing to 1210 N/mm with a lubricant containing 0.1 wt% GNPs, corresponding to an approximate 10% reduction. Compared with dry conditions, this reduction was approximately 21%. Surface roughness and 3D topography analyses further showed that GNPs-containing lubricants reduced asperities and promoted the formation of a more uniform tribofilm. At low concentrations, the improved lubrication performance of oleic acid-functionalized graphene nanoplatelets is attributed to their homogeneous dispersion in mineral oil, where physically adsorbed oleic acid improves colloidal stability by reducing agglomeration and promotes the formation of a stable tribofilm, facilitating interlayer sliding under boundary lubrication conditions. Overall, the findings demonstrate that oleic acid-functionalized GNPs, when used at optimal concentrations, significantly enhance both lubricant stability and cold rolling performance.