Flow-Line Evolution, Defect Formation, and Structure-Property Relationships in Aluminum Alloy Forging: A Review

Flow lines in aluminum alloy forgings are not merely post-deformation metallographic features; they are integrated indicators of material transport, microstructural evolution, defect susceptibility, and service performance. This review critically examines the mechanisms controlling flow-line evolution, with emphasis on constitutive flow behavior, dynamic recovery and recrystallization, second-phase redistribution, friction, thermal gradients, and die/preform design. It then evaluates how abnormal flow paths promote key defects, including folding/laps, flow-through discontinuities, vortex-like instability, and exposed flow lines, and distinguishes well-established mechanisms from topics that still rely on indirect evidence. Particular attention is given to the effects of flow-line morphology on anisotropy, notch sensitivity, corrosion-assisted damage, and fatigue life in forged aluminum alloys. Current control strategies, including preform optimization, FE-based backward tracing, multiphysics defect indices, frictional heat management, and isothermal forging, are also assessed. The available literature shows that stable contour-following flow lines are essential for the simultaneous control of defect formation, microstructural homogeneity, and durability, while major research needs remain in in situ validation, quantitative defect criteria, and digitally closed-loop process control. This review is therefore framed as a critical narrative synthesis rather than a formal systematic review; emphasis is placed on forging-centered studies that directly relate flow-path evolution to defect formation, anisotropy, fatigue, and process optimization, while evidence transferred from adjacent processes is treated as mechanistic support rather than equivalent proof.