Response Surface Modeling and Parameter Optimization of Microgroove Depth in Water-Jet-Guided Laser Machining of L605...

L605 cobalt-based superalloy is a typical difficult-to-machine material because of its high strength, pronounced work hardening, and low thermal conductivity. To improve the microgroove machining performance of this alloy, a self-developed water-jet-guided laser (WJGL) system equipped with a multi-focus lens was employed, and single-factor experiments together with a Box-Behnken response surface design were conducted to investigate the effects of laser power, pulse frequency, water pressure, and feed speed on microgroove depth. The results showed that microgroove depth increased with laser power, decreased with pulse frequency and feed speed, and first increased and then decreased with water pressure. Analysis of variance demonstrated that the developed quadratic regression model was significant and fit the data well. A recommended parameter combination of 274.9 W laser power, 3334.9 Hz pulse frequency, 1.636 MPa water pressure, and 0.107 mm/s feed speed corresponded to a predicted microgroove depth of 621.2 μm. Validation experiments yielded an average microgroove depth of 600.2 μm, with a relative error of 3.4%, indicating that the model can be used for microgroove depth prediction and parameter selection in WJGL machining of L605 alloy and may provide guidance for future multi-objective optimization considering both machining quality and efficiency.