Research Progress in the Evaluation of Thermal Shock Resistance of Refractories: From Theoretical Evolution to

Gang Wang1, Bo Ren2, Jingjing Liu3

  • 1State Key Laboratory of Comprehensive Utilization of Vanadium and Titanium Resources, Panzhihua 617000, China.

Materials (Basel, Switzerland)
|June 12, 2026
PubMed

Keywords:
energy damage theorymachine learningrefractoriessplitting testthermal shock resistance

More Related Videos

Laser-heating and Radiance Spectrometry for the Study of Nuclear Materials in Conditions Simulating a Nuclear Power Plant Accident09:18

Laser-heating and Radiance Spectrometry for the Study of Nuclear Materials in Conditions Simulating a Nuclear Power Plant Accident

Published on: December 14, 2017

A Method for Studying the Temperature Dependence of Dynamic Fracture and Fragmentation09:12

A Method for Studying the Temperature Dependence of Dynamic Fracture and Fragmentation

Published on: June 28, 2015

Related Concept Videos

Thermal expansion and Thermal stress: Problem Solving01:27

Thermal expansion and Thermal stress: Problem Solving

San Francisco's Golden Gate Bridge is exposed to temperatures ranging from -15 °C to 40 °C. At its coldest, the main span of the bridge is 1275 m long. Assuming that the bridge is made entirely of steel, what is the change in its length between these temperatures?
To solve the problem, first, identify the known and unknown quantities. The initial length (L) of the bridge is 1275 m, the coefficient of linear expansion (α) for steel is 12 x 10-6/°C, and the change in temperature (ΔT) is 55 °C.
Thermal Stress01:09

Thermal Stress

If the temperature of an object is changed while it is prevented from expanding or contracting, the object is subjected to stress. The stress is compressive if the object expands in the absence of constraint and tensile if it contracts. This stress resulting from temperature change is known as thermal stress. It can be quite large and can cause damage. To avoid this stress, engineers may design components so they can expand and contract freely. For instance, on highways, gaps are deliberately...
Thermal Strain01:19

Thermal Strain

Thermal strain is a concept that arises when we consider how temperature changes affect structures. Unlike the conventional assumption that structures remain constant under load, real-world scenarios often involve temperature fluctuations that can significantly impact these structures. Consider a homogeneous rod with a uniform cross-section resting freely on a flat horizontal surface. If the rod's temperature increases, the rod elongates. This elongation is proportional to the temperature...
Toughness and Hardness of Aggregate01:22

Toughness and Hardness of Aggregate

Toughness and hardness are critical properties of aggregate materials used in concrete, particularly on pavement surfaces and industrial flooring subjected to heavy loads. Toughness is defined as the aggregate's resistance to failure by impact and is measured by the aggregate impact value (AIV). For this, the aggregate impact value test is performed, wherein the impact is delivered by a standard hammer, which falls freely under its own weight onto the aggregates. The aggregates fragment in the...
Brick Durability, Strength, and Appearance01:15

Brick Durability, Strength, and Appearance

Brick durability, strength, and appearance are crucial factors in construction, influencing the choice of bricks for specific applications. The process of freeze-thaw, for instance, significantly affects brick durability. This phenomenon occurs when water absorbed by a brick expands as it freezes, potentially causing damage when it melts and refreezes. Bricks are graded for durability: SW-grade bricks are the most durable, offering high strength and low water absorption, followed by MW-grade...