Silicone rubber foam is widely used in multi-field engineering protection due to its excellent cushioning and thermal insulation properties. However, its performance degradation caused by long-term service aging seriously affects equipment reliability. Establishing a constitutive model that can accurately characterize the mechanical response during aging is crucial for studying performance degradation and finite element simulation. Traditional multi-parameter aging constitutive models suffer from problems such as easy convergence to local optimal solutions and poor physical interpretability of parameters. To address these issues, this study systematically characterizes the evolution laws of the stress-strain response, compression set, and stress relaxation of silicone rubber foam over an aging period of 0-768 h through accelerated thermal aging and uniaxial compression tests and proposes a second-order Ogden aging constitutive model with a single time-varying parameter. This model fixes α₁, α₂, and μ₂ as constants and only sets μ₁ as the time-varying parameter, reducing the number of parameters to be fitted from four to one. The coefficient of determination (R²) of the full-cycle stress-strain curve fitting is ≥0.9966. Meanwhile, a quantitative physical correlation between μ₁ and macroscopic aging performance indicators is established, enabling the direct prediction of the mechanical response of aged materials using measurable macroscopic indicators. This work provides an efficient and reliable modeling method for the aging performance evaluation and structural simulation of silicone rubber foam.