Organic Solvent-Free and Emulsion Self-Templating Synthesis of 3D Macroporous SiO_x/C@C for Durable Lithium-Ion...

SiO_x anodes are highly promising for next-generation lithium-ion batteries due to their superior theoretical capacity. However, issues such as drastic volume expansion and low initial Coulombic efficiency (ICE) impede their practical use. While macroporous architectures can mitigate these challenges, traditional fabrication often depends on tedious hard templating methods and significant organic solvent consumption. In this work, we report a sustainable, emulsion-self-templated and organic solvent-free strategy to synthesize a carbon-coated 3D macroporous SiO_x/C composite (3DM-SiO_x/C@C). Our approach uniquely integrates radical polymerization with a water-in-oil emulsion and sol-gel process, followed by chemical vapor deposition (CVD). The 3D macroporous framework is generated via in-situ emulsion droplets acting as self-templates, effectively eliminating the need for external sacrificial templates and toxic etchants. Notably, this organic solvent-free process achieves an exceptional precursor to (precursor + organic solvent) mass ratio of 1.0, contrasting sharply with conventional methods (0.0044-0.17). The resulting hierarchical structure, characterized by interconnected macropores and a uniform carbon coating, significantly enhances structural integrity and electronic conductivity. Electrochemical evaluations reveal that 3DM-SiO_x/C@C exhibits an improved ICE of 74.32% and long-term cycling stability even at a high current density of 1.0 A g^-1 compared to non-porous and uncoated counterparts. This integrated synthesis offers a green and scalable pathway for developing high-performance silicon-based anodes for large-scale energy storage.