Evaluation of Starch-Derived Hydrogel Systems for Artifact-Cleaning Applications

The demand for sustainable, high-performance biomaterials has driven intense research towards natural polysaccharide hydrogels. Accordingly, this study aimed to synthesize novel starch-based hydrogel materials, considering their inherent hydrogel-forming capabilities together with diverse potential applications (e.g., pharmaceuticals, medicine, and the cleaning application for the artifacts). To obtain hydrogels with enhanced mechanical and physico-chemical properties, starch was combined with other polymeric species (i.e., alginate, polyvinyl alcohol, and polyvinylpyrrolidone), and a gelling process was induced by using calcium cations or borate anions. Two distinct hydrogels (named S-Ca and S-SB, respectively) were prepared and characterized by a range of instrumental and experimental techniques. The assessed properties included water and solvent resistance, equilibrium water content, water-releasing capacity, morphology and microstructural features with their composition by SEM-EDS analysis, and mechanical properties (tensile strength, elasticity, Young's modulus, and hardness). The results indicated that the investigated hydrogels exhibited suitable properties for a variety of applications, including surface cleaning processes in the field of cultural heritage conservation. For instance, they showed equilibrium water content (between 80 and 90%) comparable with other hydrogels commonly used as cleaning tools (e.g., agar and p(HEMA)/PVP) and quite low water-releasing capacity (between 10 and 17 mgcm^-2). Moreover, the S-SB hydrogel displayed distinctly better tensile strength and elongation at break than hydrogel prepared in the presence of Ca²⁺ (S-Ca). Notably, S-SB experienced considerable elasticity improvement after freezing-thawing cycles, as indicated by a decrease in tensile strength (from 275 to 102 kPa) and an increase in elongation at break (from 121 to 275%). However, it should be noted that the hydrogel selection depends on the requirements of the target application, as different processes demand materials with distinct characteristics. Hence, both S-Ca and S-SB hydrogels were tested as cleaning tools for the removal of artificially aged acrylic coating (i.e., Paraloid B-72) from the surface of marble and wood specimens, respectively. The tests provided positive results, as aged coating was satisfactorily removed by applying the hydrogels loaded with a nanostructured emulsion (NSE). These novel starch-based hydrogels demonstrate significant potential as high-performance alternatives to conventional hydrogel systems currently used in conservation science as well as in other industrial applications.