Bio-Based Hydroxypropyl Methylcellulose Reinforced Water Glass/Silica Sol Hybrid Gel Foam with Synergistic...

To meet the requirements of forest fire prevention, a water glass-based composite gel foam was developed by introducing hydroxypropyl methylcellulose (HPMC) and nanosilica sol into a sodium silicate/sodium bicarbonate matrix. The resulting water glass/HPMC/silica sol ternary system (SGF-HPMC-SOL) was designed to improve water retention, foam stability, substrate adhesion, and fire-barrier durability. The results indicate that HPMC and silica sol contributed to network reinforcement through hydrogen bonding, polymer-chain entanglement, nanoscale filling, and possible interfacial condensation. The optimized SGF-HPMC-SOL retained 20.4% of its initial mass after heating at 100 °C for 5 h, compared with 4.65% for SGF and 9.54% for SGF-HPMC; reached a carbonization time of 164 s under direct-flame exposure, versus 100 s for SGF and 137 s for SGF-HPMC; and maintained a residual mass of 76% at 800 °C in TGA, compared with 58.3% for SGF and 55.1% for SGF-HPMC. These improvements were associated with the formation of a denser silica-rich protective layer after combustion, which delayed heat transfer to the wood substrate. Under the adopted direct-flame screening conditions, SGF-HPMC-SOL exhibited enhanced flame-retardant performance compared with the reference gel foams, indicating its potential for enhanced flame-retardant performance under laboratory screening conditions for forest fire prevention.