Terahertz Dielectric Characterization and Hybrid Debye-Lorentz Modeling of Silicone Rubber Composites for Composite...

High-temperature vulcanized (HTV) silicone rubber serves as the core material for composite insulators, and its high-frequency dielectric properties directly dictate its macroscopic insulation performance. However, traditional electrical detection methods encounter a "high-frequency blind zone" above the gigahertz (GHz) range due to limited precision and ambiguous physical mechanisms. In this study, terahertz time-domain spectroscopy (THz-TDS) was employed to characterize the complex permittivity spectra of silicone rubber specimens, incorporated with varying ratios of alumina trihydrate (ATH) and silica (SiO₂) fillers, across the 0.1-3.0 THz frequency range. Experimental results reveal that the terahertz dielectric characteristics of silicone rubber exhibit a pronounced filler dependency: as the ATH content increases from 95 phr to 185 phr, the real part of the permittivity at 1 THz increases by 32%. Notably, all specimens manifest a sharp dielectric transition near 1.2 THz, characterized by distinct dual absorption peaks in the imaginary permittivity spectra. To characterize this non-linear transition, a hybrid Debye-Lorentz model is innovatively introduced. This approach overcomes the inherent limitations of traditional double Debye models, which are restricted to relaxation processes and fail to account for high-frequency resonance. Fitting results and physical analysis demonstrate that the response at 1.2 THz is primarily attributed to the bending vibrations of Si-O-Si bonds in the polymer backbone, alongside the collective vibration modes of Al-O bonds and the hydrogen-bonded network within the fillers. The hybrid model successfully decouples three distinct polarization mechanisms: conduction loss (<0.5 THz), dipole relaxation (0.5-1.0 THz), and lattice resonance (>1.0 THz). This work provides a robust characterization framework for the quantitative evaluation of the high-frequency dielectric response and microstructural integrity of composite insulators.