Mechanical Performance and Uniaxial Compressive Behavior of Nano-TiO₂-Modified Coral Concrete

This study investigates the mechanical properties and uniaxial compression behavior of nano-TiO₂-modified coral concrete (NTCC). Twelve groups of specimens with different nano-TiO₂ contents were prepared and cured in freshwater, seawater, and oxalic acid environments. Cube compressive strength, splitting tensile strength, and uniaxial compression tests were conducted according to relevant standards. The results indicate that nano-TiO₂ significantly enhances the mechanical performance of coral concrete. The compressive and tensile strengths initially increased and then decreased with increasing nano-TiO₂ content, with the maximum strength improvement reaching approximately 22%. Furthermore, increasing the nano-TiO₂ dosage reduced the brittle failure characteristics of NTCC under compression. The curing environment had a significant influence on the performance of NTCC. Specimens cured in seawater exhibited superior early-age strength, whereas those cured in freshwater achieved the highest later-age strength. The stress-strain response of NTCC under uniaxial compression can be divided into three stages: the elastic stage, elastoplastic stage, and descending stage. Based on the experimental results, an empirical constitutive model was proposed for NTCC. The predicted stress-strain curves showed good agreement with the experimental results, demonstrating the applicability of the proposed model for describing the compressive behavior of NTCC.