Thermo-Mechanical Deformation, Jamming Risk and Life Management of Main Steam Valves in Ultra-Supercritical Steam...

Ultra-supercritical (USC) steam turbines combine severe steam conditions with increasingly frequent start-up, shutdown, and load-following operations. Their main steam valves must preserve pressure boundary integrity, sealing, and rapid actuation while non-uniform heating, creep, cyclic plasticity, oxidation, wear, and contact redistribution alter component geometry. However, the relevant evidence remains fragmented across alloy development, component thermo-mechanics, valve aerodynamics, and lifetime monitoring. This short, mechanism-oriented review integrates these domains through a material structure-function framework in which deformation relative to assembly clearance governs jamming risk. It synthesizes evidence on heat-resistant body and surface materials, 9-12% Cr steel stability, weldability and repair sensitivity, and cold, warm, and hot start-up histories. It also evaluates creep-fatigue interaction, contact, flow-induced vibration, multi-physics modeling, validation, uncertainty, monitoring, and digital twins. The synthesis shows that neither peak equivalent stress nor steady-state temperature alone can establish functional reliability. Credible assessment requires temperature-dependent material data, realistic steam-side heat transfer, cyclic constitutive behavior, initial and residual clearances, manufacturing and assembly tolerances, state-dependent friction, uncertainty analysis, and corroborating plant or inspection evidence. The most consequential research needs are valve-level validation datasets, thermal contact testing, function-oriented life criteria, and uncertainty-aware digital twins that jointly inform materials, geometry, and transient operation.