Pure gaseous-born aerogels from solid solutions via vapor sublimation and deposition polymerization

Chin-Yun Lee1, Shu-Man Hu1, Theresia Cecylia Ramli1

  • 1Department of Chemical Engineering, National Taiwan University, Taipei, Taiwan.

Nature Communications
|August 27, 2026
PubMed

More Related Videos

Preparing Silica Aerogel Monoliths via a Rapid Supercritical Extraction Method06:54

Preparing Silica Aerogel Monoliths via a Rapid Supercritical Extraction Method

Published on: February 28, 2014

Preparation of Biopolymer Aerogels Using Green Solvents08:13

Preparation of Biopolymer Aerogels Using Green Solvents

Published on: July 4, 2016

Related Concept Videos

Sublimation01:03

Sublimation

Sublimation is the direct transformation of a solid to a gaseous state. For instance, at standard pressure and room temperature, solid carbon dioxide sublimes to gaseous carbon dioxide. The phase diagram depicts the conditions required for sublimation. This process occurs at the solid-gas phase boundary and is not observed above the triple point of the substance. The reverse of sublimation is called deposition, where a gaseous substance condenses directly into a solid. Sublimation and...
Ziegler–Natta Chain-Growth Polymerization: Overview01:17

Ziegler–Natta Chain-Growth Polymerization: Overview

Ziegler–Natta polymerization is another form of addition or chain‐growth polymerization used for synthesizing linear polymers over branched polymers. The catalyst used for polymerization is the Ziegler–Natta catalyst, named after Karl Ziegler and Giulio Natta, who developed it in 1953. This catalyst is an organometallic complex of titanium tetrachloride and triethyl aluminum, with the active form of the catalyst being an alkyl titanium compound. Using the Ziegler–Natta catalyst, high molecular...
Step-Growth Polymerization: Overview01:03

Step-Growth Polymerization: Overview

Step-growth or condensation polymerization is a stepwise reaction of bi or multifunctional monomers to form long-chain polymers. As all the monomers are reactive, most of the monomers are consumed at the early stages of the reaction to form small chains of reactive oligomers, which then combine to form long polymer chains in the late stages. Hence, the reaction has to proceed for a long time to achieve high molecular weight polymers.
Many natural and synthetic polymers are produced by...
Atomic Absorption Spectroscopy: Atomization Methods01:25

Atomic Absorption Spectroscopy: Atomization Methods

Atomic Absorption Spectroscopy (AAS) atomizes samples through flame atomization or electrothermal atomization. Flame atomization typically involves a nebulizer and spray chamber assembly to combine the sample with a fuel–oxidant mixture, creating a fine aerosol mist that enters a burner. Typically, the fuel and oxidant are combined in an approximately stoichiometric ratio. However, for atoms that are easily oxidized, a fuel-rich mixture may be more advantageous. Only about 5% of the aerosol...
Recrystallization: Solid–Solution Equilibria01:10

Recrystallization: Solid–Solution Equilibria

Recrystallization is a purification technique used to separate impurities from solid compounds. In this technique, no chemical reactions occur. Instead, it exploits physical properties only, specifically, the solubility differences between the desired compound and impurities, either at a single temperature or at different temperatures, and under other selected conditions. The solid-solution equilibrium (solubility equilibrium) of each component in the solution represents a binary phase...