Synergistic Damage Behavior of 5052 Aluminum Alloy Under CW-Nanosecond Combined Pulse Laser Irradiation

5052 aluminum alloy has been widely used in aerospace, shipbuilding, automotive, and electronic industries due to its low density, high specific strength, and excellent corrosion resistance. Understanding its laser-induced damage behavior under combined continuous-wave (CW) and nanosecond (ns) pulse laser irradiation is essential for optimizing combined laser processing. In this study, the damage behaviors induced by individual CW laser, individual ns pulse laser, and combined pulse laser were systematically investigated using high-speed imaging, infrared thermography, and three-dimensional surface characterization. The results show that the combined pulse laser significantly enhances both damage depth and material removal efficiency compared with single laser irradiation. Although the peak surface temperature remains nearly unchanged under different processing conditions, the crater morphology and penetration depth vary substantially. High-speed imaging reveals that plasma evolution and molten metal ejection dominate the material removal process. Variations in processing parameters significantly modify molten pool dynamics and plasma behavior. In particular, enhanced plasma shielding or excessive energy dissipation reduces the effective laser energy coupling, leading to decreased material removal efficiency. The synergistic interaction among molten pool evolution, plasma expansion, and molten metal ejection governs the final damage morphology. This study provides new insights into the dynamic interaction mechanisms between combined pulse laser and aluminum alloys, offering guidance for parameter optimization in high-precision laser micromachining.