Sustainable Synthesis of Faujasite-Type Zeolites Synthesized from Rice Husk for Hg²⁺ Removal from Aqueous Solutions:...

Rice husk, an abundant agro-industrial by-product rich in SiO₂, represents a promising precursor for the sustainable synthesis of zeolites. In this study, rice husk ash was used to synthesize faujasite-type X and faujasite-type Y, and their performance for Hg²⁺ removal from aqueous solutions was comparatively evaluated. X-ray diffraction confirmed the successful formation of the faujasite structures, while physicochemical characterization revealed differences in pore structure and surface chemistry. FAU-type X exhibited higher Hg²⁺ removal than FAU-type Y, consistent with the combined influence of its lower Si/Al ratio, higher framework charge density and ion-exchange capacity, as well as its larger pore volume and average pore diameter. Based on its higher Hg²⁺ removal, FAU-type X was selected for a comprehensive evaluation of its adsorption performance and applicability under environmentally relevant conditions. The pseudo-second-order model best described adsorption kinetics for both zeolites, whereas thermodynamic analyses indicated that the adsorption process was spontaneous and endothermic. Optimal adsorption conditions for FAU-type X were achieved at pH 6.8, using an adsorbent dosage of 0.75 g L^-1, a contact time of 24 h, and an initial Hg²⁺ concentration of 1 mg L^-1. Equilibrium data were best fitted by the Sips isotherm model, indicating adsorption on a heterogeneous surface with a maximum adsorption capacity of 83.14 mg g^-1. FAU-type X retained appreciable adsorption performance after four regeneration cycles, although Hg²⁺ removal efficiency decreased in Caquetá River water because of competition from coexisting metal ions. To assess the environmental implications of the treated water beyond Hg²⁺ removal efficiency, ecotoxicological assays demonstrated the sensitivity of Daphnia magna to residual Hg²⁺ concentrations, whereas reductions in Escherichia coliforms were mainly attributed to the adsorption process. In addition, Lactuca sativa seedlings exhibited approximately 50% inhibition of elongation after treatment. Overall, these findings demonstrate the potential of rice husk-derived faujasite-type X as a sustainable adsorbent for Hg²⁺ removal, while highlighting the need for complementary treatment strategies to ensure the environmentally safe discharge of water and its agricultural reuse.