Zinc oxide eugenol cements. VI. Effect of zinc oxide type on the setting reactions
Journal of Biomedical Materials Research
|September 1, 1982
Abstract:
The particle size and adsorbed water on zinc oxide from various sources have been investigated and related to the reactivity with eugenol. The reactivity of zinc oxide with eugenol alone increases with the amount of water reversibly adsorbed. When 1% acetic acid is added to eugenol, the reactivity increases as the particle size of the oxide decreases. Generally, zinc oxide powders are deactivated by heat treatment because of coalescence of particles and loss of the ability to readsorb water.
Related Concept Videos
01:26EDTA: Auxiliary Complexing Reagents
EDTA titrations are usually carried out in highly basic conditions, where the fully deprotonated form of EDTA, Y4−, actively complexes with the free metal ions in the solution. Several metal ions precipitate as hydrous oxide (hydroxides, oxides, or oxyhydroxides) under these conditions, lowering the concentration of free metal ions in the solution. For this reason, auxiliary complexing agents or ligands such as ammonia, tartrate, citrate, or triethanolamine are used in EDTA titrations to...
01:24Hydration of Cement
Hydration of cement is a chemical reaction between cement particles and water. This process occurs primarily through two mechanisms: through-solution and topochemical. In the through-solution process, anhydrous compounds dissolve into their constituents, hydrates form in the solution, and then precipitate from the supersaturated solution. The topochemical process involves solid-state reactions at the cement particle surface. The through-solution process dominates the topochemical process at the...
01:12Setting Time of Cement
The setting time of cement refers to the process of cement paste transitioning from a plastic state to a solid state. This process is crucial in construction as it dictates the timeframe for concrete placement, compaction, and finishing. The onset of this solidification is termed the initial set, indicating when the paste becomes unworkable. The final set is when the paste has solidified completely, and further handling or manipulation can no longer affect its shape. The cement strength is...
01:21Types of Cement I
Portland cement comes in several types, each with distinct properties and applications based on their chemical composition and hydration characteristics:
Type I (Ordinary Portland Cement) is widely used for general construction where special properties are not required. It has moderate sulfate resistance and heat of hydration.
Type II (Modified Cement) offers moderate resistance to sulfate attack and a lower rate of heat development compared to Type I. It is suitable for structures in...
Type I (Ordinary Portland Cement) is widely used for general construction where special properties are not required. It has moderate sulfate resistance and heat of hydration.
Type II (Modified Cement) offers moderate resistance to sulfate attack and a lower rate of heat development compared to Type I. It is suitable for structures in...
01:22Types of Cement II
Portland blast-furnace cement is made by blending Portland cement clinker with granulated blast-furnace slag, which accounts for 25 to 65 percent of the cement's weight. Despite its similarities to ordinary Portland (Type I) cement in terms of fineness and setting times, its early strength is lower, though it achieves comparable strength later on. It's particularly suited for mass concrete structures and marine environments due to its lower heat of hydration and superior sulfate resistance.
01:21Pozzolans
Pozzolans are siliceous or aluminous materials blended with Portland cement. They interact with the calcium hydroxide produced during the hydration of Portland cement and contribute to improved strength and durability of concrete. The pozzolanic activity, a measure of a pozzolan's effectiveness, is typically assessed using the strength activity index, as defined in ASTM C 618-93, which calculates the ratio of the compressive strength of cement mixtures with and without pozzolan.
Fly ash is a...
Fly ash is a...