Effect of disinfection of custom tray materials on adhesive properties of several impression material systems

The effects of impression tray disinfection procedures on the bond strength of impression-material adhesives to two types of resin trays were evaluated with a tensile test. Autopolymerizing acrylic resin and a visible light-curing resin were formed into one-half inch cubes. A screw eye was attached to each cube before polymerization. Perforated trays were fabricated with stops to maintain an even one-eighth inch of impression material over the resin block. Hooks on the opposite side permitted attachment of the metal plate to a mechanical testing machine. Before adhesive was applied, one third of the resin specimens were immersed in a 1:213 iodophor solution; one third in a 10% sodium hypochlorite solution, and one third were kept in the "as fabricated" condition. Polysulfide, polyether, and polyvinyl siloxane impression material-adhesive systems were evaluated. The resin-impression material-metal plate couples were attached to a mechanical testing machine and tensile forces were applied at a separation rate of 5 inches per minute. Mean values for adhesive strength ranged from 3.49 kg/cm2 for the autopolymerizing acrylic resin/iodophor/polyether combination to 10.55 kg/cm2 for the autopolymerizing acrylic resin/untreated/polyvinyl siloxane combination. Differences were detected among materials and disinfecting procedure. Clinically, disinfection of resin trays may adversely affect retention of the impression material to the tray.