Bone bonding ability of an apatite-coated polymer produced using a biomimetic method: a mechanical and histological...

A 20-microns thick apatite layer was coated onto polyethersulfone (PES) rectangular plates by soaking them in simulated body fluid containing CaO-SiO2 based glass powder. Coated and uncoated PES plates (10 x 15 x 1.5 mm) were implanted in the tibiae of rabbits, which were sacrificed 8, 16, and 30 weeks thereafter, and the samples were examined histologically using contact microradiography (CMR), Giemsa surface staining, and a scanning electron microscope connected to an electron probe microanalyzer (SEM-EPMA). The tensile failure loads at the bone/implant interfaces were determined using the detaching test. The histological examinations showed excellent bone apposition on coated PES and the sign of degradation of the apatite layer at remodeling lacunae. The apatite layer underwent complete resorption and was replaced by bone in most areas of the bone/implant interface after 30 weeks. Bone did not bond directly to uncoated PES after each follow-up period. The failure loads between bone and coated PES at 8, 16, and 30 weeks after implantation were 1.7 +/- 0.35, 2.36 +/- 0.53, and 1.45 +/- 0.48 kg, respectively. Those between bone and uncoated PES were nearly 0 kg at each postimplantation period. Failure during the detaching test occurred at the bone/apatite interface or near it after 8 weeks. After 16 weeks, it usually occurred at the apatite/ PES interface or near it, and occasionally in the middle of the apatite layer. The apatite layer was hardly detected at the failured interface after 30 weeks. In this study, an apatite-coated PES produced using a biomimetic method was demonstrated to bond directly to bone without any intervening soft tissue, which indicates that this material possesses excellent bioactivity.