In vitro properties of a chitosan-bonded self-hardening paste with hydroxyapatite granules

A new self-hardening paste was made by using a combination of chitosan, hydroxyapatite (HA) granules, ZnO, and CaO. The sol was made by dissolving 0.1 g of chitosan in a solution of 0.1 g malic acid and 2.0 mL physiological saline solution. Mixed with 0.03 g of CaO and 0.04 g of ZnO powders was 2.77 g (55 wt %) of HA granules which had a homogeneous pore distribution and a porosity of 35-48%. The size of the granules was set for 0.1-0.3 mm. Kneading and setting of the paste generated a little amount of heat (32.8 degrees C) as compared with the heat produced by polymethyl-methacrylate (PMMA) bone cement (114.5 degrees C). The pH value of chitosan-HA-hardened composite after setting was nearly equal to that of human plasma (pH 7.4), while that of PMMA bone cement maintained an acid pH of 4.7. Hydroxyapatite granules less than 0.1 mm, 0.1-0.3 mm, or 0.3-0.6 mm were set using chitosan sol. The size of the granules did not influence the compressive strength of the set chitosan-HA-hardened composite. The greatest compressive strength of chitosan-HA-hardened composite was obtained by using 55 wt % of HA granules. The strength of the chitosan-HA-hardened composite was comparable to that of the cancellous bone derived from tibial eminentia, but was considerably lower than that of the PMMA bone cement.