Changes in surface hardness of conventional restorative glass ionomer cements

The effect of a contact with an aqueous solution on the surface hardness of glass ionomers has been investigated in a few studies and for a limited number of formulations. As there is no information on the long-term changes of the surface hardness in this respect, the aim of this study was to determine these long-term changes in 10 conventionally setting glass ionomer formulations after storage in water as compared to maturation in a humid atmosphere (85% RH). After setting for 15 min different series of glass ionomer specimens were stored at 37 degrees C in both experimental media for 1, 7, 28 and 140 days. At the end of the specific maturation times, the mean surface hardness was determined on the basis of Knoop Hardness (KHN). Data were analyzed using ANOVA. In a humid atmosphere the surface hardness generally increases rapidly initially, followed after 1 day by a more gradual increase. In contact with water, the hardness also increases up to one day but not to the same extent. The surface hardness then remains constant or slightly decreases. Evidence of a detrimental softening of the surface ascribed previously to the loss of matrix forming ions was not found. A surface erosion is not likely to occur.