Shear strength of dentin and dentin bonded composites

E Mondragon1, K J Söderholm

  • 1Department of Dental Biomaterials, College of Dentistry, University of Florida, 1600 SW Archer Road, Gainesville, FL 32610-0446, USA.

The Journal of Adhesive Dentistry
|January 24, 2002
PubMed
Abstract

More Related Videos

Shrinkage of Dental Composite in Simulated Cavity Measured with Digital Image Correlation08:45

Shrinkage of Dental Composite in Simulated Cavity Measured with Digital Image Correlation

Published on: July 21, 2014

Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material07:42

Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material

Published on: December 20, 2024

Related Concept Videos

Problem Solving on Stress and Strain01:22

Problem Solving on Stress and Strain

Stress is a quantity that describes the magnitude of a force that causes deformation, generally defined as internal force per unit area. When forces pull on an object and cause its elongation, like the stretching of an elastic band, it is called tensile stress. When forces cause the compression of an object, it is known as compressive stress. When an object is being squeezed uniformly from all sides, like a submarine in the depths of the ocean, we call this kind of stress bulk stress (or volume...
Shearing Stress01:18

Shearing Stress

Shearing stress, denoted by the Greek letter tau (τ), is stress caused by forces acting transversely on an object. These forces create internal ones within the entity in the plane where the external forces are applied. The resultant of these internal forces is the shear in the section.
The average shearing stress can be calculated by dividing the shear by the area of the cross-section.
Strength of Cement01:20

Strength of Cement

Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in ASTM C...
Bonding and Strength of Aggregate01:12

Bonding and Strength of Aggregate

The bond between aggregate particles and the cement matrix is significantly influenced by the shape and surface texture of the aggregates. High-strength concretes benefit from a rougher texture, which leads to stronger bonding due to greater adhesion. Angular aggregates with larger surface areas also enhance this bond. The bonding quality, however, is complex to assess as no universally accepted test exists. Good bonding is indicated when a crushed concrete specimen shows some aggregate...
Tensile Strength Considerations of Concrete01:16

Tensile Strength Considerations of Concrete

Considering the tensile strength of concrete involves recognizing that the theoretical strength of cement paste can be up to a thousand times higher than what is observed in practical applications. This significant discrepancy is largely attributed to the presence of microscopic cracks within the concrete. These cracks tend to amplify stress at their tips when a load is applied, a phenomenon explained by Griffith's theory of brittle fracture.
The dimensions and shape of a concrete specimen also...
Relation Between Tensile Strength and Compressive Strength of Concrete01:30

Relation Between Tensile Strength and Compressive Strength of Concrete

Concrete is a fundamental building material, and understanding its strengths is crucial for construction projects. The relationship between its tensile and compressive strengths is intricate, showing that while these strengths are related, they do not increase at the same rate. Tensile strength's growth is slower and is affected by various factors such as the methods used for testing, the size and shape of the specimen, the texture of the aggregate used, and the moisture content of the concrete.